Colour: dark grey. Density: 14.5 g/cm3.
Hardness: HRA 91.5.Grain size: 0.8um
Bending strength: 2800 N/mm².
Raw material: YG10X with 10% CO content and 0.8um grain size.
Coating: Altin, high aluminum content provides excellent hot hardness and oxidation resistance.
A good choice for milling the general steels weaker than HRC 45. But due to the aluminium content, it is not a good choice for aluminium.