●ca. 860 g Sn90Zn7Cu3 Felder Stangenlot ( 2002/95/EG 2000/537EG )
●Für Flamm- und Kolbenloetungen für den KFZ-, Rohr-, Blech-, Kühlungsbau u.a -bereich
●Metallische Zusammensetzung: 90 % Sn, 7% Zn, 3 % Cu
●Schmelzbereich: ca. 220– 250 °C Arbeitstemperatur: ca. ca. 220– 250 °C
●MADE IN GERMANY! 1A-Handwerkerqualität vom Markenhersteller Felder

[4 Stangen ca. 860 g]

Description

The solder has a very large melting area and is therefore also suitable for soldering on built-in body parts. It is characterised by its optimal gap filling, good wetting on steel, the lowest lunker formation in the soldering process, as well as good abrasionability and its high strength. The zinc content in this lead-free body solder provides a pasty consistency when applying and spraying and prevents the solder from dripping off at vertical solder points. The processing temperature should be in the melting area of the alloy to achieve optimal consistency. The shape as a pressed flat bar has an additional, positive influence on the workability when applying. .
Metallic composition : 90 % SN, 7 % Zn, 3 % Cu
Melting range/point: 200 – 250 °C
Rated weight: 7.6 g/cm3 working temperature: approx. 200 - 250 °C